고분자량의 poly(1,4-butylene carbonate-co-terephthalate) 합성과 열적 성질
- Alternative Title
- Lee Jung Jae
- Author(s)
- 이정재
- Alternative Author(s)
- Lee Jung Jae
- Advisor
- 이분열
- Department
- 일반대학원 분자과학기술학과
- Publisher
- The Graduate School, Ajou University
- Publication Year
- 2014-02
- Language
- eng
- Keyword
- biodegradable polymer; comspostable polymer; PBCT; PBAT; 생분해성 고분자; polyester; polycarbonate; 폴리에스터; 폴리카보네이트
- Alternative Abstract
- Condensation copolymerizations of 1,4-butanediol (BD), dimethyl carbonate (DMC), and dimethyl terephthalate (DMT) were conducted by a two-step procedure using sodium alkoxide (0.1–0.2 mol%) as a catalyst with a variable [DMT]/[BD] feed ratio. In the first step, oligomers bearing almost equal numbers of hydroxyl and methoxycarbonyl end-groups were generated, which were polycondensed mostly by the elimination of methanol at 190¬–210 °C under reduced pressure. By this procedure, high-molecular-weight poly(1,4-butylene carbonate-co-terephthalate)s (PBCTs) were easily prepared with Mw 60000¬–200000 in a reasonably short reaction time (~8.5 h) and even on large scale (110 g polymer/batch) in a 250 mL glass reactor. The PBCTs prepared at a high [DMT]/[BD] feed ratio 0.30¬–0.50 were semi-crystalline polymers with fast crystallization rates and melting temperatures in the range 95−146 °C, which were adjustable by the [DMT]/[BD] feed ratio. The glass transition temperatures were rather high around 0 °C. These thermal properties were comparable to those of commercialized compostable polyesters such as PLA, PHA, PBAT, and PBSA.
- Fulltext
- Appears in Collections:
- Graduate School of Ajou University > Department of Molecular Science and Technology > 3. Theses(Master)
- Files in This Item:
- There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.
-
- License
- STATISTICS
- Total Visit :4,070,713
- Total Download :1,967
- Today View :1,143