Polystyrene Chain Growth Initiated from Dialkylzinc for Synthesis of Polyolefin-Polystyrene Block Copolymers
- Alternative Title
- Tae Jin Kim
- Author(s)
- 김태진
- Alternative Author(s)
- Tae Jin Kim
- Advisor
- 이분열
- Department
- 일반대학원 분자과학기술학과
- Publisher
- The Graduate School, Ajou University
- Publication Year
- 2020-02
- Language
- eng
- Alternative Abstract
- Polyolefins (POs) are the most abundant polymers; however, synthesis of PO-based block copolymers has only rarely been achieved. We aimed to synthesize various PO-based block copolymers by coordinative chain transfer polymerization (CCTP) followed by anionic polymerization in one-pot via conversion of the CCTP product (polyolefinyl)2Zn to polyolefinyl-Li. Addition of 2 equiv t-BuLi to (1-octyl)2Zn (a model compound of (polyolefinyl)2Zn) and selective removal or decomposition of (tBu)2Zn by evacuation or heating at 130 °C afforded 1-octyl-Li. Attempts to convert (polyolefinyl)2Zn to polyolefinyl-Li were unsuccessful. However, polystyrene (PS) chains were efficiently grown from (polyolefinyl)2Zn; the addition of styrene monomers after treatment with t-BuLi and pentamethyldiethylenetriamine (PMDTA) in the presence of residual olefin monomers afforded PO-block-PSs. Organolithium species that might be generated in the pot of t-BuLi, PMDTA, and olefin monomers, i.e., [Me2NCH2CH2N(Me)CH2CH2N(Me)CH2Li, Me2NCH2CH2N(Me)Li·(PMDTA), pentylallyl-Li(PMDTA)], as well as PhLi(PMDTA), were screened as initiators to grow PS chains from (1-hexyl)2Zn as well as from (polyolefinyl)2Zn. Pentylallyl-Li(PMDTA) was the best initiator. The Mn values increased substantially after the styrene polymerization with some generation of homo-PSs (2729%). The Mn values of the extracted homo-PS suggested that PS chains were grown mainly from polyolefinyl groups in [(polyolefinyl)2(pentylallyl)Zn][Li(PMDTA)]+ formed by pentylallyl-Li(PMDTA) acting onto (polyolefinyl)2Zn.
- Fulltext
- Appears in Collections:
- Graduate School of Ajou University > Department of Molecular Science and Technology > 3. Theses(Master)
- Files in This Item:
- There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.
-
- License
- STATISTICS
- Total Visit :3,755,853
- Total Download :1,818
- Today View :2,045